溶剂脱沥青掺配FCC油浆技术改造
Retrofit of Solvent Deasphalting Blending FCC Slurry
-
利用族组成分析、FTIR、1HNMR和13cNMR考察了FCC油浆及其经溶剂选择性多级萃取后得到的富芳馏分(FCCRF)的组成结构变化。
Using of group composition analysis , FT-IR , ~ 1H-NMR and ~ ( 13 ) C-NMR , the composition of FCC slurry and aromatics enriched fraction ( FCCRF ) by multiple extraction were investigated .
-
油浆过滤装置自动控制在DCS上的实现
Realization of Automatic Control for FCC Slurry Oil Filtration System on DCS
-
FCC油浆富芳馏分的热解
Pyrolysis of aromatic enrichment fraction of FCC slurry oil of Bay
-
减压渣油与FCC油浆共炭化的化学组成变化
Composition changes in the CO-CARBONIZATION OF FCC slurry and VR
-
FCC油浆热转化制备中间相沥青的研究
Preparation of Mesophase Pitch by Thermal Conversion of FCC Slurry
-
FCC油浆糠醛抽出油改善胶粉改性沥青性能的研究
Performance improvement of crumb rubber modified asphalt with FCC slurry furfural extract
-
减压渣油搀兑FCC油浆制备针状焦
Preparation of needle coke from FCC slurry blended vacuum residue
-
延迟焦化加工FCC油浆的经济和技术分析
Techno-economic analysis for processing FCCU slurry in delayed coker
-
FCC油浆糠醛加助剂预处理工艺
Pre-treatment Catalytic Cracking Slurry With Furfural Adding Compound Agent
-
本文成果为FCC油浆的进一步利用提供了理论和应用技术参考。
This paper provides a theoretic and applied reference to the further utilization .
-
FCC油浆芳烃富集前后的反应性
Reactivity of FCC slurry before and after aromatic enrichment
-
FCC油浆的分离与综合利用
Separation and complex utilization of FCC oil slurry
-
FCC油浆提高废胶粉改性沥青热存储稳定性试验
Pretreat crumbled rubber with FCC slurry to improve hot storage stability of modified bitumen
-
FCC油浆下游产品开发研究
Development of downstream product of FCC slurry
-
煤与FCC油浆共处理重质产物对道路沥青改性作用的评价
Evaluation of heavy products from co-processing of coal and FCC slurry for paving asphalt modification
-
本研究结果可为FCC油浆在沥青路面工程中的应用提供依据,具有重要实际意义。
The research provided valuable demonstration for fluid catalytic cracking slurry application in asphalt pavement construction .
-
计算所得选择性表明糠醛是分离FCC油浆的有效溶剂。
The selectivity calculated shows that furfurol is an excellent extraction solvent for separating FCC slurry .
-
不锈钢粉末烧结滤芯脱除FCC油浆中催化剂粉末中试研究
Pilot plant test of removing catalyst fines from FCC slurry with sintered stainless steel filter core
-
SF-2催化裂化油浆防垢剂的工业应用
Commercial application of SF-2 antifoulant for FCC slurry system
-
以催化油浆为增孔剂的MCM-41介孔分子筛的合成
Synthesis of MCM-41 mesoporous molecular sieves with FCC decant oil as swelling agent
-
馏分油浆态床加氢处理研究:ⅡFCC柴油加氢工艺条件及动力学研究
A study on process for slurry-bed hydrotreating of distillate oil : ⅱ Processing conditions and kinetics analysis of FCC diesel oil
-
经过桐油、糯米汁改性粘土的土工特性FCC油浆糠醛抽出油改善胶粉改性沥青性能的研究
PERFORMANCE OF CLAY IMPROVED WITH TUNG OIL AND STICKY RICE JUICE Performance improvement of crumb rubber modified asphalt with FCC slurry furfural extract
-
试验以预处理的FCC油浆为原料,采用程序升温、多管井式坩埚炉进行热转化形成有序生长中间相反应研究。
Orderly growth of mesophase was studied using FCC slurry as raw materials , in a multi-tube well-crucible furnace controlled by programmed heating .
-
采用配方均匀设计方法,制定试验方案,对FCC油浆与丙脱沥青调合生产重交通道路沥青进行试验研究。
FCC slurry blending with the asphalt from propane deasphalting unit to produce heavy traffic paving asphalt has been tested by adopting uniform recipe design scheme .
-
通过偏光显微镜观察了石油系油浆(LH)与煤系闪蒸油(SN)焦化后所得焦块的光学结构。
Lump cokes obtained from petroleum ( LH ) and coal based products ( SN ) were examined by the reflected polarized light microscope .
-
而大量的FCC油浆外甩导致部分可裂化的烷烃、芳烃等理想组分进入油浆,从而造成FCC原料的损失。
This makes part of alkane and aromatics , which are the ideal components for the refinery , into the slurry oil causing the FCC feedstock loss .
-
废胶粉用FCC油浆进行预处理后用于沥青改性,制备出沥青与胶粉间相容性好、高温存储性能稳定的胶粉改性沥青。
The FCC slurry is used to pretreat crumbled rubber to improve compatibility of bitumen and crumbled rubber and produce crumbled-rubber modified bitumen with good hot storage stability .
-
以FCC油浆和丙脱沥青为原料,采用配方均匀设计方法,进行调合生产重交通道路沥青的研究。
The experiment of producing heavy traffic paving asphalt was carried out with the FCC slurry and the propane deasphalted asphalt as the feedstock by uniform prescription design method .
-
未经处理的原料只观察到了小球的出现与固化,而预处理FCC油浆可以观察到中间相小球出现、长大、融并及固化的完整过程。
And the formation , growth , coalescent and solidify of mesophase spherule was continuously observed , while the slurry without pretreatment only showed the formation and solidify of the mesophase spherule .