本文主要介绍改性石英填料的粘度、浸润性能（渗透时间、浸润角、浸润点等）等指标，以及表面改性效果的评价方法。

In terms of viscosity , osmosis time , contact angle and oil absorption this paper evaluates the effect of surface modification of mineral filling .

本文用显微镜和扫描电镜，研究了金属与合金对小颗粒人造金刚石浸润角的测定方法。

This paper deals with the influence of metal and alloy on the measurement of wetting angle of microdot artificial diamond by means of microscopy and scanning electron microscopy .

研究结果表明：Au-Ag-Si系钎料合金与Ni润湿性良好，随着钎焊温度的增加，铺展面积增加，浸润角减小；

The results show that the Au-Ag-Si brazing filler metal series have a good wettability with Ni .

黄土的浸润角略大于30°。

In addition , the soggy angle of loess is found to be slightly larger than 30 ° .

测量结果表明，浸润角与系统温度间有相关性，并与整体陶瓷与液态纯金属间的测量结果相吻合。

It is shown in the measuring results that there is a correlation between the wetting angle and the system temperature , and the results are similar to that obtained from the block ceramics and liquid pure metal .

局部浸润麻醉下行下颌角肥大及颧骨突出磨削术

Prominent Mandibular Angle and High Malar Grinding of the Bone Under Local Anaesthesia

通过与传统的加热搅拌改性方法的比较，微波辅助改性方法在浊度、浸润度、接触角等方面都优于传统改性方法。

By compared to the traditional modification method of heating and stirring , the microwave aided method has many advantages on cloudiness , soakage , contact angle etc.

实验表明，Ni对Nb表面的浸润性能良好，在1368℃时，浸润角为21°。

Experimental results indicate that Nb is wetted well by Ni with the wetting angle of 21 ° at 1368 ℃ .

通过活性钎料Ag66Cu30Ti4对ZrO2的浸润试验测定了钎料／陶瓷界面反应产物、浸润角和反应层厚度与温度的关系。

The wetting test of active solder Ag 66 Cu 30 Ti 4 to ZrO 2 was studied in this paper . The interfacial product of solder ceramic was defined and the dependence of wetting angle and reaction layer thickness on temperature was obtained .