潜伏性固化剂

  • 网络latent curing agent;latent hardener
潜伏性固化剂潜伏性固化剂
  1. 采用化学改性合成的间甲苯胺改性双氰胺衍生物作为环氧树脂潜伏性固化剂,通过差示扫描量热法(DSC)研究了间甲苯胺改性双氰胺/环氧树脂E-44体系的固化反应。

    The dicyandiamide derivative modified by m-toluidine was used as latent curing agent of epoxy resin . Curing reactions of epoxy resin system containing modified dicyandiamide were studied with differential scanning calorimetry ( DSC ) .

  2. 改性双氰胺类环氧树脂潜伏性固化剂的研究及其应用

    Study on latent curing agent of modified dicyandiamide for epoxy resin and its application

  3. 新型环氧树脂潜伏性固化剂的合成及性能研究

    Study on Synthesis and Properties of Novel Latent Curing Agents for Epoxy Resin

  4. 席夫碱金属配合物固化剂是一类新开发的环氧树脂潜伏性固化剂,用其固化环氧树脂能显著提高树脂固化物耐热性能、力学性能。

    Schiff base metal complex is a novel kind of latent curing agent for epoxy resins .

  5. 咪唑类潜伏性固化剂

    Imidazole Type Latent Curing Agent

  6. 初步固化实验结果表明,这种环氧树脂潜伏性固化剂具有较好的固化性能。

    The results showed that the new curing agent has good stability at room temperature and improved curing performance .

  7. 本文用重氮树脂光敏剂与聚乙烯醇、粘合剂、潜伏性固化剂配伍,研制成新型圆网感光材料。

    The new sensitive material of rotary screen was prepared with diazo-colophony photosensitizer and polyethylene alcohol , epoxy adhesive , delitescent solidified agent .

  8. 潜伏性环氧固化剂的发展

    Development of Latent Curing Systems to Epoxy Resin

  9. 研究结果表明,有机脲类化合物ND作为快速潜伏性环氧树脂固化剂,在环氧粉末涂料中加入4%时,固化温度为180℃,粉料55秒可以完全固化。

    ND , which is a rapid latent epoxide resin , solidified agent and accelerator , is a kind of organic urea compound . When 4 wt % ND is added to epoxy powder coating , it can be solidified in 55 sec .

  10. 改性咪唑类潜伏性环氧树脂固化剂的制备

    Preparation of Modified Imidazole Latent Curing Agent for Epoxy Resin

  11. 新型潜伏性环氧树脂固化剂的研制

    The synthesis and characterization of a new latent curing agent of epoxy resin

  12. 热失重分析结果表明产物基本达到了作为潜伏性环树脂固化剂的要求。

    The result of TG indicates that the product can meet the requirement of a good latent epoxy resin Curing agent .

  13. 新型潜伏性M-DDM微胶囊固化剂的制备及表征

    The Fabrication and Characterization of a Novel M-DDM / Microcapsule-Type Latent Curing Agent