真空蒸发法

本论文对真空蒸发法和直流溅射法沉积锌膜的工艺进行了研究，结合XRD、SEM、AFM等分析手段，以探索这两种方法在制备锌膜方面的一般规律。

The techniques of depositing zinc thin film on grass substrate by vacuum evaporation and direct-current sputtering were investigated with XRD , SEM and AFM in this paper .

采用真空蒸发法，在载玻片上制备了SnS薄膜。

Thin films of SnS were deposited by means of vacuum evaporation .

以V2O5粉末为原料采用真空蒸发法结合真空退火还原法在玻璃基片上制备VOx薄膜，调节不同的基片温度获得几组薄膜。

VO_x thin films are prepared on glass by means of evaporation of V_2O_5 powder and post annealing in vacuum .

用真空蒸发法在玻璃和单晶硅片上制备纯Zn和掺杂Zn薄膜，然后在高于450℃条件下进行氧化、热处理（玻璃衬底）获得良好的纳米ZnO薄膜和掺杂ZnO薄膜。

Zn thin films and impurity dopped films were prepared by vacuum evaporation on glass and silicon substrates to obtain the nanon ZnO films on the oxidize and heat treatment over 450 ? ℃ in O 2 ( glass substrates ) .

用真空蒸发法在普通玻璃衬底以及镀有共面梳状A1电极的玻璃衬底制备了多晶PbI2薄膜。

The polycrystalline lead iodide films were fabricated on normal transparent glass and normal glass coated with aluminum electrode like a bar by evaporation growth in vacuum chamber .

采用界面渐进冷冻浓缩法和真空蒸发法分别对柠檬汁进行界面渐进冷冻浓缩和真空蒸发浓缩。

Lemon juice was concentrated by progressive freeze concentration and vacuum evaporation respectively .

这种方法的合成速度比传统的真空蒸发法快10倍以上，适合工业化生产。

The production rate by using this method is10 times or more larger than that by the conventional vapor evaporation method , so this method is suitable for industrial production of nanoparticles .

用真空蒸发法、分子镀法和离心沉积法制备92Mo同位素氧化物靶，介绍了各法的优点、存在的问题和解决途径。

In order to prepare a target of 92 MoO 3 , vacuum evaporation , centrifuge precipitation and molecular plating techniques are used . The advantages , problems as well as its solution are discussed for three methods .

目前，制备CIO薄膜的方法很多，包括真空蒸发镀膜法。

At present , the CIO films can be prepared by many methods and one of them is coating by vacuum evaporation-oxidation method .

采用真空热蒸发法分别在玻璃、单晶硅（111）、（100）和二氧化硅片上制备CdO薄膜和稀土镝掺杂CdO薄膜并对薄膜进行热处理。

We prepare pure CdO and Dy-doping CdO thin films by vacuum evaporate-deposition on different substrates , such as glass , Si and SiO_2 , furthermore take heat treatment the films .

论述了采用DTB型结晶器从工业粗制芒硝中制取无水硫酸钠的工艺条件以及采用真空蒸发结晶法的原因。

In this paper the technological crystallize condition of get anhydrous sodium sulfate from the industry coarse decahedrons sodium sulfate by using DTB crystallize is discussed , and the reason why the vacuum evaporation crystal used is given .

真空热蒸发法在线有机包覆铜纳米颗粒

Preparation of the Organic Coating Around Cu Nanoparticles by Heating Evaporation

真空共蒸发法沉积的ZnTe：Cu薄膜

ZnTe : Cu Films Deposited by Vacuum Co - evaporation

用真空共蒸发法在室温下制备了ZnTe：Cu多晶薄膜。

ZnTe : Cu films were deposited by vacuum co-evaporation technique at room temperature .

采用真空蒸发沉积法在经过粗糙化前处理的镍箔和铜箔上分别沉积硅薄膜。

Using the vacuum vapor deposition method , the Si film was deposited on the Ni and Cu foil roughed by pre-treatments .

运用真空微蒸发镀覆法、直接氧化法及溶胶&凝胶法在磨料表面镀覆了Al、Si、Ti、TiO2和Al2O3。

By means of vacuum slow vapor deposition , oxide directly and sol-gel techniques Al , Si , Ti , TiO2 or Al2O3 films were coated on the surface of the grains .

真空蒸发和滚轧法能获得自支撑靶的最小厚度分别为80和560μg/cm~2。

The minimum thickness of 50 and 560 μ g / cm ~ 2 of Fe targets could be obtained with vacumm evap-oration and rolling respectively .