硬质合金模具

  • 网络Tungsten carbide nib
硬质合金模具硬质合金模具
  1. DT钢硬质合金模具材料的研究

    Study on Model Material of Hardening Alloy With DT Steel

  2. WC-Ni系大直径无磁硬质合金模具的研制

    Development of Large Diameter , Non magnetic WC Ni Cemented Carbide Die

  3. 根据逆向工程中的造型和注塑模具的设计要求,用UG/MoldWizard对注塑模具进行设计、UGNX对模具型腔进行数控编程实践。我国硬质合金模具应用技术与市场分析

    Based on the request of the construction and injection mold designing , the designing , manufacturing is practiced in UG / Mold Wizard and UG NX . APPLICATION TECHNIQUE AND MARKET ANALYSIS OF CEMENTED CARBIDE DIE SET IN CHINA

  4. 硬质合金模具翻新工艺工具接头的硬合金抗磨圈

    Renewed technology of hard metal alloy mould tool joint hard band

  5. 我国硬质合金模具应用技术与市场分析

    Application technique and market analysis of cemented carbide die set in China

  6. 硬质合金模具翻新工艺硬质合金可转位刀具

    Renewed technology of hard metal alloy mould indexable carbide insert cutting tool

  7. 钢结硬质合金模具热处理及应用

    Heat Treatment and Application of Steel Structure Cemented Carbide Die

  8. 冷镦钢球用硬质合金模具的失效分析

    Failure Analysis of Carbide Dies Used for Cold Upsetting Balls

  9. 硬质合金模具翻新工艺木工硬质合金圆锯片

    Renewed technology of hard metal alloy mould carbide-tipped circular sawblade for wood working

  10. 钢结硬质合金模具的锻造工艺

    Forging Technique of the Steel Bonded Hard Alloy Die

  11. 磁芯模具;陶瓷元件模具;硬质合金模具。

    Magnetic core die , discrete ceramic die , and cemented carbide die .

  12. 钢结硬质合金模具冷热加工工艺研究

    The Research for Cold & Heat Processing of Steel Bond Hard Alloy Mould

  13. 硬质合金模具翻新工艺

    Renewed technology of hard metal alloy mould

  14. 硬质合金模具计算机管理网络系统

    Computer control network system of hardmetal mould

  15. 小规格螺钉冷镦用硬质合金模具的性能研究

    Machining of Dies and Molds Die and Mould Technology Study of hard alloy dies property for cold heading small screw

  16. 铜管拉拔用硬质合金模具表面摩擦磨损分析以及使用寿命研究

    Analysis of the Wear and Friction on the Surface of Carbide Cemented Drawing Die for Copper Tube and Research on Service Life

  17. 我们的经营理是为硬质合金模具加工企业提供完美的技术解决方案、降低生产成本、提高工作效率。

    Our business philosophy is to provide perfect technology solution , to reduce production costs and enhance work efficiency for carbide die processing enterprises .

  18. 着重从冲片排样、导向和定位、凸凹模设计方面介绍了高速冲床用硬质合金模具设计,同时对提高冲片精度的措施和模具加工方法也作了介绍。

    This paper introduces the design of die & mould for high-speed punching machine , the measures for improving precision and the processing method is also involved .

  19. 对硬质合金模具在实际设计和制造方面取得实效的一些经验和方法,进行归纳总结并作系统介绍,以供参考。

    Both some experience and methods which have achieved actual effect in design and manufacture for hard metal die are classified , summarized and introduced systematically , so as to be a reference to people .

  20. 改进了冷拔钢管所需硬质合金模具的加工工艺,采用电化学腐蚀法和机械法相结合,既节省加工时间,又减少了投资费用,并实现了电蚀机床一机多用。

    The improvement on processing of carbide dies for steel pipe cold-drawing involves a combination of electrochemical erosion method with machining , which leads to reduction of both machining time and investment as well as the multi-use of the electroerosion machine tool .

  21. 通过对硬质合金模具失效形式与使用寿命的关系的调查及对合金模芯的疲劳断口形貌、合金低倍与高倍组织的检测,认为在模具失效的多种形式中,疲劳断裂是主要的。

    Through the investigation of the relation between failure mode and service life of carbide dies , as well as inspection of fatigue fracture appearance of die cores and microstructure of carbide , it is shows that the main mode of die failure is fatigue fracture .

  22. 硬质合金拉拔模具的失效分析

    Failure Analysis of Cemented Carbide Drawing Die

  23. 本文针对常规超硬复合体烧结模具的缺点,借鉴硬质合金压制模具的结构形式,对超硬复合体烧结模具结构进行优化。

    This paper aims at the shortcomings of normal sintering mould of composite body and , inspired by the structure of tungsten carbide mould , optimizes the mould structure of super hard composite body .

  24. 用合金堆焊模具,是在普通碳结构钢的基体上堆焊合金钢或硬质合金作为模具工作部分,以提高模具寿命及耐用度,降低模具成本。

    Bead welding dies with alloy is a way to bead weld alloy steel or hard alloy on the normal carbon structure steel matrix used as the woking area , so that the life and durability of dies can be improved and the cost can be reduced .

  25. 本文介绍了热力学和动力学分析预测在TRIP钢,硬质合金以及塑料模具钢研制中的应用,从而为现代先进材料的设计提供参考。

    Thermodynamic analyses , and sometimes coupling with kinetic estimation , to TRIP steels , cement carbides and mold steel for plastics are shown in the effort to designing modern advanced materials .

  26. 硬质合金粉末压制模具的设计

    Design of Press in g Mould of the Hard Alloys Powder

  27. 硬质合金冷镦螺钉模具的性能研究

    The Study of Hard Alloy Dies Property for Cold Heading Small Screw

  28. 钢结硬质合金冷作模具硼-硫复合渗强化工艺

    Reinforcement Process of Cold Working Steel Bonded Carbide Dies by Surface Boronizing and Sulfurizing

  29. 电镜观察显示热疲劳是硬质合金热挤压模具失效的主要原因。

    The SEM observation shows that thermal fatigue is the major cause of the failure of the steel hard alloy die .

  30. 脆性断裂是钢结硬质合金冷变形模具的主要失效形式。

    When the die of steel-bonded carbide is used in cold working , brittle fracture is the main form of losing its efficiency .