乳浊釉
- 网络opaque glaze
-
结果表明:为获得较高白度及良好釉面性状的低温快烧分相乳浊釉,少量B2O3的添加是必需的。
The study demonstrates that addition of a little amount of B 2O 3 is indispensable to obtain fast fired phase-separative opaque glazes with high whiteness and good surface properties .
-
快烧无锆分相乳浊釉的形成
Formation of fast fired phase-separation opaque glazes with no zirconium
-
添加少量F~-和P2O5对锆乳浊釉熔块中锆溶析行为的影响
Effects of Small Amount of F ~ - and P_2O_5 additives on the Melting and Crystallization Behaviour of Zirconium in Frit of Zirconic Opaque Glaze
-
B2O3对R2O-RO-B2O3-SiO2-Al2O3系统快速烧成乳浊釉分相过程的影响
Effect of B_2O_3 on the Phase-Separation Process of Fast-Fired Opaque Glazes in R_2O-RO-B_2O_3-SiO_2-Al_2O_3 System
-
R20-RO-Al2O3-SiO2-P2O5系分相/析晶乳浊釉乳浊粒子的形成机理
Forming Mechanism of Opacifying Particles of Phase-Separative / Crystalline Opaque Glaze in R_2O-RO-Al_2O_3-SiO_2-P_2O_5 System
-
米氏(Mie)理论在锆乳浊釉中的应用研究
Application of Mie Theory to Opacification of Zircon Glaze
-
利用XRD、TEM、高温显微镜等测试手段,初步研究了骨灰对卫生瓷乳浊釉工艺性能的影响以及骨灰乳浊釉的乳浊机理。
XRD , TEM and high temperature microscope were used to analyze the effect of bone ash on the technological properties of porcelain milky glaze .
-
借助于XRD分析和SEM分析,发现该系统乳浊釉为分相乳浊釉,主要乳浊相为分相液滴。
We found that the glaze belonged to opalescent glaze of splitting glass phase , and the primary opalescent phase was glass drops by XRD and SEM analysis .
-
以Sb掺杂的SnO2半导体为导电填料,选取透明釉、钡无光釉、锆乳浊釉为基釉进行了防静电陶瓷的研制。
The anti-static ceramic tiles were prepared by adding Sb-doped SnO 2 into three different base glaze - transparent glaze 、 barium mat glaze and zirconium opaque glaze .
-
利用SEM、XRF等测试手段对高档卫生洁具用乳浊釉进行了研究分析,结果表明乳浊釉中的气孔是导致釉面粗化的主要原因,结合实验结果,探讨了细化乳浊釉面的途径。
The opaque glaze is analysis by SEM 、 XRF , the results point out it is the bubbles that make the glaze course . The paper discussed the way to prepare fine and smooth opaque glaze according to experiment .
-
工业废渣在复合无光乳浊釉中的应用
Application of industrial slag in preparation of composite Matt opaque glaze
-
锆英石乳浊釉及其添加剂的影响
The emulsifiable glaze made of zircon and effect of different additives
-
一种低温无硼无铅生料乳浊釉的研究
Study on Low Temperature Boron free and Leadless Raw Opaque Glaze
-
低温快烧自生微晶乳浊釉的研究
Study on a Spontaneous Crystalline Opaque Glaze Fired Fast under Low Temperature
-
低成本一次烧无锆钙质无光乳浊釉的研制
Preparation of low-cost once fired Zirconium-free calcium opaque Opacified Glaze
-
锆英石乳浊釉乳浊性能的影响因素
Facts that Affect the Opal Property of the Opaque Glaze with Zircon
-
磷灰石对锆乳浊釉性质的影响
Effect of Apatite on Properties of Emulsifiable Glaze of Zircon
-
日用瓷用锆乳浊釉的研制
Research and Manufacture of Zirconic Emulsion Glaze for Domestic Ceramics
-
快速烧成低锆固-液复相乳浊釉的研究
Study on fast-fired low zirconium solid-liquid multiphase opaque glaze
-
用低锆流纹岩研制乳浊釉
Manufacture of Emulsified Glaze with Low - zirconium Rhyolite
-
通过合理设计釉组成,研制出了一种不含锆英石微粉的生料乳浊釉。
A zircon-free raw opaline glaze with appropriate chemical composition has been developed .
-
骨灰对卫生瓷锆乳浊釉工艺性能的影响及其乳浊机理研究
Effects of bone ash on the technological properties of porcelain zirconium milky glaze
-
用低锆流纹岩作为乳浊釉中的乳浊剂,获得了成功。
Low-zirconium rhyolite has been successfully used as emulsifier in manufacturing emulsified glaze .
-
低成本快速烧成硼锆乳浊釉的研究
Study on Fast - fired boron - zirconium opaque glaze of low cost
-
中、高温钛乳浊釉显微结构的研究
Studies on the Microstructure of Ti-Opaque Glazes at Moderate or High Firing Temperature
-
低温快烧的钛乳浊釉
Titanic quick firing opalescent glaze at low temperature
-
一种多次分相乳浊釉及其乳浊机理
Opaque Glaze with Separated-Phases And Its Opaque Mechanism
-
磷灰石在乳浊釉中应用的研究
Study on Application of Phosphorite in Opacified Glaze
-
组成及工艺条件对分相/析晶乳浊釉乳浊行为的影响
Effects of composition and process conditions on opacifying behavior of phase-separative / crystalline opaque glaze
-
并获得了效果理想的复合乳浊釉。
The ideal opacity glaze was obtained .