固体酒精

用工业酒精制取固体酒精燃料

Preparation of Solidified Alcohol Fuel With Industral Alcohol

固体酒精的制备研究&制备过程中影响因素的分析

Research on Preparation of Solidified Alcohol & Analysis of accessible factors on the preparation

研究中发现固体酒精为多孔结构，孔径为1~14μm，估计由直径为150nm的溶胶粒子堆积而成；

In this research , we found the solid alcohol is porous , the aperture about 1 ~ 14 μ m , which is accumulated by particles with diameter about 150nm ;

用40mL酒精溶解2.0g硬酯酸，50mL酒精溶解0.4g氢氧化钠，在70℃下反应30min，制备的固体酒精综合性能最好。

The solid alcohol had the best properties when the preparation conditions were as follows : stearic acid 2.0 g in 40 mL alcohol , sodium hydroxide 0.4 g in 50 mL alcohol , reaction time 30 min , reaction temperature 70 ℃ .

优质固体酒精的研制与性能实验

The Performance Test and Production for Solid Alcohol of High Quality

均匀设计法优化固体酒精的制备工艺

Study on the optimum conditions of solid alcohol using homogenous design

固体酒精的制备工艺与性能研究

Research on Preparation Process and Performance of Solid Alcohol

固体酒精制备工艺条件的研究

Research on Technological Conditions for Preparation of Solid Alcohol

固体酒精燃料生产工艺的改进

Improvement of Productive Technology of Solid Alcohol

固体酒精合成新工艺

A new process of preparing solidified alcohol

固体酒精制取工艺的改进

An Improvement of Preparing Technique Solidified Alcohol

固体酒精最佳投料比的研究

Best Inventory Ratio of Solid Alcohol

固体酒精的研制

Development of the Solid Alcohol

醋酸钙和硬脂酸钠为固化剂研制固体酒精

The Development of Solid Alcohol

采用体视显微镜、熔点管、黏度计、电导率仪和分光光度计等仪器研究了固体酒精的溶胶-凝胶过程。

The study of the solid alcohol 's Sol-Gel Process by stereoscopic microscope , melting point tube , viscometer , conductivity meter , et al .

运用酒精、硬脂酸、氢氧化钠、酚酞、硝酸铜、硝酸钴等原料，制备彩色固体酒精。

The colored solidified alcohol has been prepared by utilizing alcohol , stearic acid , sodium hydroxide , phenolphthalein , copper nitrate and cobalt nitrate .

制得的固体酒精的熔点为52℃，燃烧时仍保持固体状态。

The solid alcohol prepared under this condition has a melting point of 52 ℃, and the solid alcohol of 150 g burns in solid state continuously for 114 min.

介绍了固体酒精燃料生产工艺的改进试验，利用工业酒精、硬脂酸、石蜡、硝酸铜为主要原料，开发出具有实用价值、安全、卫生、方便的固体酒精燃料。

This paper introduced an improved technique in the production of practical , safe , hygienic and convenient solid alcohol with industrial alcohol , stearic acid , paraffin , cupric nitrate as main materials .

介绍了分别以醋酸钙、硬脂酸钠为固化剂，研制安全、卫生、方便的固体燃料酒精的方法。

This paper takes acetic acid calcium , hard fatty acid sodium as the solidification pharmaceutical separately , and develop two kinds of security , hygiene , convenient solid fuel & solid alcohol .

在高温（55℃）条件下，应用CSTR反应器对含高浓度悬浮固体的木薯酒精废水进行了全渣厌氧处理研究。

Continuously stirred tank reactor ( CSTR ) was used for thermophilic anaerobic treatment of cassava ethanol wastewater with high-concentration suspended solids at55 ℃ .