炭黑粒子

SEM分析表明，炭黑粒子被包埋在SBR基体中，无游离炭黑存在。

The analysis on SEM showed that the N 330 dispersed uniformly in the rubber matrix without free carbon black particle .

SEM分析表明，P（CR/SRF）粒子表面和内部尚存在部分未被包覆的游离炭黑粒子是造成接触污染性的主要原因。

SEM analysis showed that the free carbon black existing in the surface and inner of P ( CR / SRF ) particles was the main reason for the contact-pollution .

单一纳米炭黑粒子链的拉伸强度为（4.5±2.5）MPa，杨氏模量为3.0~8.8MPa。

The tensile strength of a single nanoparticle chain aggregate of carbon black is ( 4.5 ± 2.5 ) MPa , and its Yang 's modulus is 3.0 ~ 8.8 MPa .

研究表明，聚丙烯酸接枝改性炭黑粒子表面的zeta电位远低于未接枝改性的炭黑粒子；但由聚丙烯酰胺接枝改性炭黑粒子的表面zeta电位值不发生明显的变化。

The experimental results show that the zeta electric potential of carbon black particles modified with surface graft polyacrylic acid is lower than one of unmodified carbon black , but modification of surface grafting of acrylamide onto carbon black do not change zeta electric potential of unmodified carbon black particles .

聚合物接枝改性炭黑粒子表面性质研究

Study of surface properties of carbon black particles modified with surface grafting polymer

另外，炭黑粒子分布的不均匀性导致了海绵的体积电阻率较高。

The uneven dispersion of CB in foam results in higher volume resistivity .

炭黑粒子表面功能化及其应用

Functionalization of carbon black surface and Its Applications

聚丙烯酰胺在炭黑粒子表面的功能修饰及其在传感领域的应用

Functionalization of carbon black partical surface from polyacrylamide and its applications to sensing fields

研究了含有微细炭黑粒子混和单体悬浮聚合产物的粒径及形貌特性。

The particle diameter and surface characteristics of toner particles prepared by suspension polymerization in the presence of carbon black particles were studied .

GB/T14853.3-1993橡胶用造粒炭黑粒子磨损量的测定高频感应熔覆制备耐蚀耐磨涂层研究

" Rubber compounding ingredients Carbon black , pelletized Determination of pellet atrition " Study on Anticorrosion and Antiwear Coatings Manufactured by High Frequency Induction Cladding

响应的重复稳定性受炭黑粒子分散行为的影响，从聚合物溶胀行为及逾渗导电理论解释了实验结果。

The reproducibility of the electric resistance is influenced by the dispersion behavior of CB . The experimental results are explained in the view of the swelling of the polymer chain and percolation theory .

当填充量达到一定程度时，炭黑粒子之间开始相互作用，在体系中形成了类似链状和网状的形态，称为导热网链。

When the filling amount has reached certain degree , the carbon is interacted each other , the net and similar chain is formed in the system , which is called thermal conductivity net chain .

在机械搅拌和超声场共同作用下，使纳米炭黑粒子均匀地分散到醇酸调和漆和醇酸防锈漆中，制得纳米炭黑复合涂料。

Nanometer carbon black dispersion system in ultrasonic field was put into alkyd resin coating and alkyd resin antirust coating respectively , and then nanometer composite coating was obtained by means of ultrasonication and ( mechanical ) agitation .

进一步分析得出，硫化胶性能得以改善的根本原因是La3+改善了炭黑粒子在橡胶基体中的分散均匀性及其与橡胶基体的黏结牢固性。

Detail analysis led to the point that the improved properties of vulcanizates are substantially due to the La3 + which improves the dispersed uniformity of carbon black particle in the rubber matrix and the adhesion between carbon black particle and rubber matrix .

在超声场作用下，将接枝改性及缩醛化反应制备的油溶性纳米炭黑粒子（24nm~300nm）加入到普通油漆中，获得了纳米炭黑复合涂料。

In ultrasonic field , nanocomposite coating was got by adding oil-soluble carbon black nanoparticles synthesized by surface graft modification into paint . SPM image and TEM picture showed that the particle size was about 24 nm to 300 nm and dispersed uniformly in coatings .

从抵抗高温气流冲蚀、抗炭黑粒子化学侵蚀和抵抗炉气杂质化学侵蚀等三个方面对高纯刚玉砖、刚玉莫来石砖、铬刚玉砖、高铬砖和氧化锆砖作了分析比较。

The high temperature gas impact resistance , carbon black corrosion resistance as well as slag corrosion resistance abilities of high purity corundum brick , mullite-corundum brick , corundum-chrome brick , high chrome brick and zirconia brick lined on high temperature carbon black reactor are discussed , respectively .

GB/T3780.16-1983炭黑单个粒子压碎强度的测定

Carbon black & Determination of individual pellet crush strength

掺杂聚苯胺与气相白炭黑复合粒子的研究GB/T14853.6-1993橡胶用造粒炭黑单个粒子破碎强度的测定

Composite Particles of Doped Polyaniline and Pyrogenic Silica " Rubber compounding ingredients Carbon black , pelletized Determination of individual pellet crushing strength "

炭黑原生粒子表面由细小的石墨状晶体无规排列构成，并存在富勒结构碳，呈凹凸不平的原子台阶形貌。

The surface of primary particle of CB consists of randomly ranged fine graphite-like crystals with Fullerene structure carbon , and shows rough atomic steps ' morphology .

研究了由聚合物表面接枝改性炭黑和氯化钾水溶液组成的分散体系中炭黑粒子表面zeta电位的变化。

The surface zeta electric potential of carbon black particles modified with surface grafting polymer and KCl aqueous solution system was investigated .

PE/炭黑导电复合体系正（电阻）温度系数用接枝炭黑作导电粒子研究了在聚乙烯基材中的正（电阻）温度系数（PTC）效应。

PTC Characteristics of Polyethylene / Carbon Black Conductive Composites Composites based on grafting carbon black / polyethylene were prepared to study the positive temperature coefficients properties .

在炭黑密相气力输送试验的基础上，考察了输送后炭黑粒子的破碎率，研究了影响其破碎率的主要因素。

The influence factors of particle breakage of carbon black were investigated based on the test of dense phase conveying .

研究了LDPE/LLDPE作为载体树脂对黑母粒炭黑分散性的影响，通过薄膜的透过率测定、相差照片和炭黑粒子粒度分布情况评价了LLDPE的加入对炭黑粒子的分散性的改善情况。

The effect of blends of LDPE / LLDPE as a carrier resin in black masterbatch was studied . Adding the LLDPE into the resin can improve the dispersion of carbon black through testing the ratio of light permeation and watching the discrepancy photo and analyzing the distribution of particles .

与炭黑填充极性聚合物相反，表面含氧量高的炭黑在HDPE中更容易凝聚形成网络，非极性HDPE链段对炭黑的束缚作用随炭黑粒子表面含氧量的增加而减小。

On contrary to carbon particles-filled polar polymer composites , CB with higher surface oxygen content was easier to agglomerate and form networks in HDPE , and the effect that CB particles were confined by HDPE chains becomes weak with increasing the surface oxygen content of CB .