硅丙乳液

  • 网络silicone-acrylate emulsion;silicon-acrylic latex
硅丙乳液硅丙乳液
  1. 结果表明,采用半连续法和种子预乳化法制得的硅丙乳液,冻融稳定性比较好,经过冻融循环后可以复原;

    The result showed that the silicon-acrylic latex , which was made by semicontinuous process , seed pre-emulsification , had good freeze thawing stability , and would back to status quo after freeze thawing recycle .

  2. 通过IR、TG等手段表征合成硅丙乳液,验证硅丙乳液的热稳定性随着有机硅含量的增加而升高。

    By using IR , TG to characterize the synthesis of silicon-acrylic latex , verify the thermal stability of silicon-acrylic latex improved with silicone content increases .

  3. Mg(OH)2纳米材料杂化硅丙乳液的制备与表征

    Preparation and Characterization of Silicone-Acrylic / Nano-Mg ( OH ) _2 Hybrid Emulsion

  4. 采用四氯化钛为原料合成TiO2纯水性溶胶,将TiO2溶胶和硅丙乳液通过加热、温度控制等制备了水性光催化自洁涂层液。

    Titanium oxide sol was prepared by using titanium tetra-chlorid e.Water-photocatalysis self-cleaning coating was prepared with TiO 2 sol and silicopropane emulsion by heating and temperature control .

  5. 利用红外光谱、透射电镜、DSC等分析手段,对硅丙乳液的粒子结构进行了表征,并与乳胶漆的主要性能进行了关联、分析。

    By means of IR , GPC , TEM and DSC , molecular structure of silicone acrylate emulsion was characterized , correlated with principal performance of emulsion paint and analysed .

  6. 在普通水泥砂浆中加入硅丙乳液配制成聚合物改性水泥砂浆(PMC),并对其性能和微观结构进行了研究。

    Polymer modified cement mortar ( PMC ) was formed by adding siloxane / acrylate copolymeric emulsion in the Portland cement mortar . The mechanical properties and the micro structure of PMC were investigated .

  7. 采用K2S2O8热引发体系合成了有机硅改性丙烯酸酯微乳液,实现了硅丙乳液乳胶粒子的超微细化。

    The poly ( siloxane-acrylate ) microemulsions were synthesized using K 2S 2O 8 as initiator and copolymer nanoparticles were obtained .

  8. 实验结果表明制备的最佳工艺条件为硅丙乳液加入量为25%(Wt%),TEOS:MTES:C2H5OH:AMP-95:NH3·H2O摩尔比例为1:4:30:0.63:10,室温反应6h。

    Results showed that the optimal conditions for preparation of acrylic emulsion dosage were silicone acrylate emulsion 25 % ( Wt % ), the molar ratio of TEOS : MTES : C2H5OH : AMP-95 : NH3 · H2O was 1:4:30:0.63:10 , 6h at room temperature .

  9. 采用后添加VTES法制得的硅丙乳液,其吸水率则随VTES用量的增加而升高,冻融循环后发生破乳。

    The water absorption of silicon-acrylic latex , which was made by post adding VTES , increased as the VTES content increased , and the emulsion was broken after freeze thawing recycle .

  10. 高性能硅丙乳液无皂制备技术的研究

    Study on preparation technology of high performance soap-free silicone acrylic emulsion

  11. 无皂硅丙乳液的耐候性、耐水性等优良。

    The weatherability and water resistance of the emulsion are better .

  12. 硅丙乳液型防水织物胶粘剂的研制

    Preparation of Waterproof Textile Coating Agent of Organosilicon / Acrylic Latex

  13. 高性能硅丙乳液研究进展

    Advance in Research of Silicone - acrylate Emulsion with High Performance

  14. 硅丙乳液共聚涂料对石质文物保护的应用研究

    Application Research on Silicon-acrylate Copolymer Emulsion for Lithoid Cultural Relic Protection

  15. 硅丙乳液外墙涂料的类型、配制和施工

    The Type , Manufacturing , Construction of Silicon-Acylic Latex Outer Wall Coatings

  16. 建筑防水涂料用硅丙乳液的制备与性能

    Preparation and properties of siloxane acrylate latex building waterproof coating

  17. 高稳定性硅丙乳液合成及性能的研究

    Synthesis and Properties of High Stability Silicone Modified Acrylate Emulsion

  18. 高性能无皂硅丙乳液合成的研究

    Study on the Copolymerization of High Performance Soap-Free Silicone-acrylic Emulsion

  19. 烷基糖苷的物化性质及在硅丙乳液聚合中的应用

    Alkyl Polyglycoside 's Physical and Chemical Properties and Application in Silicone-acrylic Emulsion

  20. 纳米粘土对硅丙乳液的改性

    Modification of Silicone - acrylate Latexes by Nano Clay

  21. 硅丙乳液聚合稳定性能研究&聚合工艺条件的影响

    Research on stability of silicone-acrylic emulsion polymerization - Effect of Polymerization process condition

  22. 自交联硅丙乳液聚合稳定性的研究

    A Study of Polymerization Stability of Self-Crosslinked Silicone-Acrylate Emulsion

  23. 硅丙乳液合成过程及产品性能影响因素的研究

    Study on Influence Factors of Synthesis Process and Product Properties of Silicone-acrylic Emulsion

  24. 硅丙乳液超薄型钢结构防火涂料的制备

    Preparation of Silicone-acrylate Emulsion Ultrathin Steel Structural Fireproofing Coating

  25. 功能化硅丙乳液的应用基础研究

    The Applied Basic Research of Functionalized Silicone-Acrylic Latices

  26. 核壳结构硅丙乳液的研制及纳米改性研究

    Preparation of Core-shell Structure Organosilicon Modified Acrylic Composite Emulsion and Study on the Nano-modification

  27. 本文讨论了有机聚硅氧烷分子的分子结构对硅丙乳液性能的影响;

    Influnce of molecular structure of organopolysiloxane on properties of silicone acrylate emulsion was discussed .

  28. 膨胀型硅丙乳液防火涂料

    Expanding silicones-acrylate emulsion fire protective coating

  29. 改性硅丙乳液合成及高耐候性外墙乳胶涂料制备的研究

    Study on the Synthesis of Organosilicon-modified Acrylic Emulsion and Preparation of Exterior Paint with High Weather-durability

  30. N-羟甲基丙烯酰胺对硅丙乳液及乳胶膜性能的影响

    The Influence of N-Hydroxymethyl Acrylamide on Properties of Modified Arylate copolymer latex with Organosilicon and Latex Film