铁素体不锈钢在氧化物燃料电池中的应用

Ferritic Steel Interconnect Used in Solid Oxide Fuel Cell

本文研究了铁素体不锈钢（F201）与低碳钢（Q235A）对接采用TIG：焊和手工焊时，选用不同的焊接材料对焊缝成形和性能的影响.试验结果表明。

Studies the effects of different welding materials on weld appearance and welded joint properties in the butt welding of ferritic stainless steel ( F201 ) with low carbon steel ( Q235A ) using TIG ( gas tungsten arc welding ) or manual welding method .

430铁素体不锈钢TiN形核细化凝固组织的研究

Study on Solidification Structure Refining of 430 Ferrite Stainless Steel with TiN Nucleation

目前研究和使用的合金有三种：Cr基合金、Ni基合金和铁素体不锈钢。

Now , three kinds of alloys were studied and applied : Cr-former alloy , Ni-based alloy and the ferritic steel .

铁素体不锈钢焊接HAZ的晶粒长大模型

Modeling of grain growth in HAZ of a ferrite stainless steel

冷轧工艺对SUS430铁素体不锈钢塑性应变比r值的影响

Effect of Cold Rolling Process on Plastic Strain Ratio - r of SUS 430 Ferrite Stainless Steel

TCS铁素体不锈钢采用奥氏体型焊材，实芯焊丝、药芯焊丝和电焊条方法，焊接接头力学性能可以满足使用要求。

With austenitic welding material , solid wire , flux-cored wire and electrode , welded joint mechanical property of TCS ferritic stainless steel all can meet usability .

从理论上研究了TiN在430铁素体不锈钢钢液中和凝固过程中析出的热力学条件。

The thermodynamics of TiN precipitation in liquid steel of 430 ferrite stainless steel during its solidification was calculated to find out the condition of TiN precipitation during the initial solidification stage .

409L铁素体不锈钢的表面钝化膜性能

Properties of Surface Passivating Film of Ferritic Stainless Steel 409L

Fe-Cr-Mo系铁素体不锈钢在氯化物介质中的实验电位-pH图研究

An investigation of the experimental potential-pH diagrams for Fe-Cr-Mo ferritic stainless steels in chloride media

利用超声振荡空蚀实验机对Cr-Mn-N奥氏体-铁素体不锈钢进行了空蚀研究。

The cavitation erosion behavior of Cr-Mn-N austenite-ferrite stainless steel was investigated by ultrasonic vibration cavitation erosion equipment .

本文计算了温度、压力与合金元素的浓度对Fe-Cr-Mo系铁素体不锈钢C-O反应平衡的影响，所得结果表明降低压力、提高熔炼温度均对碳氧反应有利，增高铬的含量有不利影响。

The effect of temperature , pressure and alloy concentration on the equilibrium of carbon-oxygen reaction for a ferritic Fe-Cr-Mo stainless steel was investigated .

一钢公司1780热轧具有集中批量轧制、铁素体不锈钢与碳钢混合轧制等特点，因此ORG技术的应用显得极为重要。

The hot rolling process was characteristic of pooled-batch rolling and mixed rolling of carbon steel & SUS grades , it was very important that the ORG technique was applied to the hot strip rolling .

[方法]通过金相、SEM和EDAX等先进显微分析技术及化学成份和机械性能检测等方法对封头-进口铁素体不锈钢棒进行检验和分析。

Using Metallographic , SEM , EDAX and other chemical and mechanical methods , imported ferrite stainless steel bars are detected and analyzed . It is found that there are a large number of sulfured manganese inclusions inside the sample bars .

为了开发同质芯冷却水口，采用适宜规格同质芯冷却水口对SUS430铁素体不锈钢进行板坯模拟试验研究。

Casting SUS 430 stainless steel with cooling nozzle that has proper homogeneous core size was simulated to investigate the optimum design of cooling nozzle .

通过对洗衣机外筒缺陷样品的化学成分、金相组织检测以及断口能谱分析，讨论了用SUS430铁素体不锈钢制作洗衣机外筒产生裂纹的原因；

The forming cause of crack in washing machine outer barrel made from 430 ferrite stainless steel is studied by analyzing chemical composition , metallographic structure and EDS.

中间试验线轧制试验表明，经过不同温度热轧后的430铁素体不锈钢都存在晶间腐蚀敏感性，其中空冷的DL-EPR试验Ra值比水冷的高，敏感性也更严重。

Intermediate test line rolling experiment showed that the susceptibility of intergranular corrosion existed at different temperatures after hot rolling , which the air cooling is more severe of sensitivity with the DL-EPR test Ra value was higher than the water-cooled .

高铬铸铁磨球的研制铁素体不锈钢的进展

High Chromium Cast Iron Grinding Balls Development of Ferritic Stainless Steels

铁素体不锈钢焊接区域的组织特征

Characteristics of Microstructure in Welding Zone of the Ferritic Stainless Steel

铁素体不锈钢熔化焊晶间腐蚀的探讨

Research in Ferritic Stainless Steel Grain Boundary Corrosion during Fusion Welding

合金元素对铁素体不锈钢抗腐蚀性能的影响

Effect of Alloying Elements on Corrosion Resistance of Ferritic Stainless Steel

开发抗菌铁素体不锈钢可行性研究

The feasibility study on exploiting germ resistance ferrite stainless steel

特种软质铁素体不锈钢的研制

Research and development of a special soft ferritic stainless steel

稀土元素对430铁素体不锈钢冲击韧性的影响

Effect of Rare Earth on Impact Toughness of 430 Ferrite Stainless Steel

关于铁素体不锈钢焊接晶间腐蚀的若干问题

On Some Problems for Ferritic Stainless Steel Grain Boundary Corrosion During Welding

铁素体不锈钢管子管板焊接工艺研究

Study on the Welding Procedure of Ferrite Stainless Steel Tube to Tubesheet

超纯430铁素体不锈钢组织和性能的研究

The Study on Structure and Property of Ultra-pure 430 Ferritic Stainless Steel

铁素体不锈钢连铸板坯宽度尺寸的控制

Breadth control of continuous casting slabs for ferrite stainless steel

铁素体不锈钢在国外已大量应用于铁路车辆。

Ferritic Stainless Steel has been broadly used on manufacture of Railway Vehicle .

抗菌处理对含铜铁素体不锈钢组织和性能的影响

Effects of Antibacterial Treatment on Microstructure and Properties of Copper-bearing Ferritic Stainless Steel