测试结果表明，镀层48h中性盐雾试验、155℃8h恒温试验和270℃15s高温试验，外观无明显变化；

The test results show that after 48 h neutral salt spray test , 8 h constant temperature test at 155 ℃ and 15 s high temperature test at 270 ℃, the deposit has no obvious changes ;

本文通过高温试验和扫描电镜分析，研究三种典型烟煤在800～1600℃条件下，其焦炭的膨胀性、流动性、软化现象、孔隙结构及其活性。

This paper studys three types coal coke 's distensibility , mobility , ruckbildung , the structure of pore and activity by high temperature test and SEM . The three cokes come from three typic coal which react in the temperature ranging from 800 to 1600 ℃ .

利用X射线衍射分析了上述4种薄膜在高温试验前后的物相结构变化。

X-ray diffraction was used to analyze the change of microscopic physical structure of the four films before and after the experiments .

采用不同的高温试验工艺对T91钢管的TIG焊接头进行处理，分析TIG焊接头在力学性能和显微组织上的差异。

Mechanical property and microstructure of T91 steel pipe joint with TIG welding on different high-temperature test process was researched .

高温试验：研究了持续高温（23～35℃）对20～100kg生长育肥猪生产性能、蛋白质和能量代谢、PD、LD、HP及能量利用的影响；

High temperature trials : the performance , nitrogen and energy metabolism , PD , LD , HP and energy utilization of 20-100 kg growing-finishing pigs were measured in constant hot temperature ( 23-35 ℃), respectively ;

用DTA研究了OM2的热分解温度。用IR和XPS等方法研究了高温试验后产物的结构变化以及成膜试片表面的元素组成。

Thermal discomposing temperature was determined by DTA , and the change of structure and element composition of surface film with inhibitor after high temperature tests were studied by means of IR and XPS etc.

利用动态有限元法对分离式拉伸Hopkinson杆高温试验中的误差进行了分析。着重考虑了由输入和输出杆上的温度梯度引入的误差。

By means of dynamic finite element method ( DFEM ), the error in the split Hopkinson tension bar test at temperature gradient is analysed and the error from the temperature gradient in the input and output bar is considered particularly .

这种金属经过了高温试验。

As a test the metal was subjected to great heat .

混凝土的高温试验技术和高温力学性能研究

Study on Concrete of Experimental Technique and Mechanical Property at High Temperature

结构用钢的高温试验研究

Experimental research of structural steel at elevated temperature

GB/T4098.7-1983射频电缆高温试验方法

Test method of high-temperature for radio-frequency cables

轴向约束钢筋混凝土异形柱的高温试验研究

Experimental study on axially restrained reinforced concrete columns with special shaped cross sections under fire

在高温试验的中期进行了为期6~14天的消化代谢试验。

During the metaphase of high temperature experiment , digestive and metabolic experiments were conducted for6 to14 days .

通过地铁盾构隧道管片1/3缩尺寸模型的火灾高温试验，分析了火灾中管片截面温度场的分布规律。

Through the fire test of one-third scale model segment , the regularity of temperature field of segment section is analyzed .

根据中国药典的规定，对盐酸青藤碱控释微丸的稳定性进行考察，包括影响因素试验（高温试验、高湿试验、强光照试验）、加速试验和长期试验。

Influencing factors including high temperature , high humidity and strong light were investigated . Accelerated test and long-term test were conducted .

在此工作基础上，本文还设计了高温试验方案，并对温度加载及测量控制系统进行了测试，验证了方案的可行性。

Based on the above work , high-temperature test scheme is designed and validated by testing the thermal loading and the measurement control system .

通过数值分析与高温试验的对比参照，研究了隧道管片在不同温度-荷载工况下的力学性能变化。

Through comparing the numerical analysis with reference to high-temperature test , changes of mechanical properties of shield tunnel segment under different thermal-mechanical conditions are studied .

检测通过剪切、拉伸、冲击、弯曲、耐水性、高温试验、储存稳定性找出最好的固化剂和配比。

Detection through the shear , tensile , impact , bending , water resistance , high temperature testing , storage stability to find the best curing agent and its ratio .

通过长期运行，考核冷却孔设计，骨架和蒙皮强度是否适用，蒙皮抗堵塞性能，蒙皮与骨架的焊接性能，以及试验台对高温试验的适应性。

Through long-term operation , the application of cooling hole design and skin strength , property of skin blockage , weld performance of skin and framework , and adaption of test table to high temperature is examined .

方法：对照组用生理盐水，实验组用提取的多糖按生药量20g/kg对小鼠连续灌胃后进行耐缺氧试验、游泳试验及耐高温试验。

METHODS : Control group was used physiological saline , experimental group was used extracted polysaccharides of 20 g · kg - 1 dosage , and to carry out resist anoxic test , swimming test and resist heat test .

积分分离模糊PID控制器在高温湿热试验控制系统中的应用

The Application of Integral Apart Fuzzy PID Control in the High Temperature and Humidity Control System

通过高温氧化试验研究了热浸镀铝钢合金层硬度的变化规律，借助电子探针和X－射线衍射仪对合金层的成分、形貌和氧化产物进行了分析。

The principle of alloy layer hardness of hot dip aluminized steels have studied with high temperature oxidation test .

高温硬度试验证明二次硬化效果是由M（23）C6碳化物形成引起的。

The results of the hardness test prove the effect ot secondary hardening in cau - sed by forming M_ ( 23 ) C_6 carbides .

ABOw/SnO2/6061Al合金基复合材料的高温拉伸试验

Hot Tensile Experiment of ABO_w / SnO_2 / 6061Al Alloy Composites

本文介绍了SiH4/PH3混合气体的高频辉光放电法，在硅、玻璃衬底上淀积的掺P氢化非晶硅膜的结构和特性，并对样品作了高温退火试验。

The P - doped a-Si : H film is deposited on substrate of silicon and .

耐热钢FNA组合焊接接头的高温强度试验研究

High Temperature Strength Test of Heat Resisting Steel FNA Combined Welded Joint

这样的SiC涂层系统经受了长达30h以上的高温氧化试验和多种动态环境模拟试验而保持完整无损，显示了优良的性能和长的使用寿命。

After undergoing 30-hour high temperature oxidation and many environment simulating experiments , this SiC coating system still maintains excellent integrity .

本文采用高硅4032铝合金材料，利用Gleeble-1500热模拟试验机，进行了高温压缩试验。

Isothermal compression tests of 4032 aluminum alloy were performed on Gleeble-1500 thermal simulator .

GLEEBLE材料热模拟试验机高温压缩试验的数据整理与修正

The collating and correcting of data in hot compressing test for Gleeble material hot modeling test machine

经高温耐磨试验和切削试验证明，M3滚刀经TiN涂层后，其耐磨性和使用寿命显著提高。

It is concluded that the resistance to wear and the life of the hob have been improved greatly through the test of high temperature resistance to wear and the cutting test .