底釉

通过密着性能测试及扫描电镜（SEM）对搪瓷界面的形貌观察和能谱分析，研究了纳米Al2O3粉末对搪瓷锑钼底釉密着性能的影响。

The effect of nanometer Al 2O 3 powder on the adherence of the Sb-Mo enamel was studied through the adhesive test . Scanning electron microscopy and energy dispersive X-ray spectroscopy were used to study the microstructure of the enamel-steel interface .

红坯陶瓷砖底釉的开发应用

The Development of the Ground Glazes for Red Ceramic Tiles

提高锑钼底釉密着性能的研究

Studies on Improving the Adherence of Sb-Mo Enamel to Steel

钢板日用搪瓷白底釉日用钛白釉瓷层耐酸性能研究

Study on Acid Resistance of Titania - white Domestic Enamel

锑钼底釉的磨加效应

Effect of Mill Additives on Sb-Mo Enamel Ground Coats

钢板日用搪瓷白底釉

White Ground Coat for Domestic Sheet Steel Enamel

萤石在底釉中的作用

The Role of Fluorspar in Ground Enamels

其工艺基础为底釉、面釉分别制备，三次施釉，一次烧成。

The process is based on producing ground glaze and surface glaze in difference , spraying glaze three times , firing one time .

增加基体表面粗糙度和减小面釉在底釉中的含量，可促进润湿性的改善。

The wetting performance can be improved with the increase of surface roughness of base metal or with the decrease of the content of overglaze in priming glaze .

本课题设计了底釉和面釉两种配方，底釉能够与不锈钢基体有效结合以缓解热膨胀系数方面的差异，而面釉则可以通过调整配方组成来达到耐磨、耐腐蚀的性能要求。

The bottom-glaze can combine with the stainless steel effectively and alleviate the thermal-expansion coefficient differences between them , while the surface-glaze can achieve the requirement of wear-resistance and corrosion-resistance .

研究结果表明，底釉的润湿面积随着温度的升高和恒温时间的延长而增大，在一定的温度和时间下达到最大值。

The results indicate that the wetting area of priming glaze will enlarge with increasing temperature and insulation time , and achieve the greatest value at 900 ℃ and insulation time of 1000 seconds .

结果表明，在底釉、面釉中各加入1.5%磷酸银，烧成温度约940℃，可制得杀菌效果良好、耐久的搪瓷。

These research results show that the better bactericidal effect and endurance can be achieved by adding 1.5 % silver phosphate in the ground and cover caot , and controlling the firing temperature about 940 ℃ .

涂层破坏的主要原因是和腐蚀介质接触的底釉层首先被腐蚀掉，然后面釉层在残余应力的作用下断裂、塌陷，被分解为小碎片。

The main cause of the failure was that the bottom layer contacts with the corrosion solution was eroded first , which induced fracture of the upper layer under the action of residual stress and break into shivers .

治疗前及治疗3个月和6个月后拍摄全口曲面断层片，记录釉牙骨质界到骨缺陷底及釉牙骨质界到牙槽嵴顶的距离；

In the two patient groups , routine clinical examination of the subjects was performed to record periodontal attachment level and distances of CEJ to the bottom of the bone defects and to the alveolar crest before and 3 and 6 months after the treatment .