对竹浆常规过氧化氢（H2O2）漂白工艺进行了研究。

In this paper , conventional H2O2 bleaching of Bamboo pulp are studied .

另外还进一步还探讨了竹浆H2O2强化的臭氧漂白工艺。

In addition , ozone bleaching of bamboo pulp with addition of H_2O_2 was also discussed .

对硫酸盐竹浆臭氧漂白的影响因素进行了研究，并通过正交实验得出臭氧单段漂白的最佳工艺条件为浆浓10%，臭氧用量0.5%，温度20℃和pH值2。

In this paper , some factors , which influenced ozone bleaching of kraft bamboo pulp , were studied with the orthogonal test .

高卡伯值硫酸盐竹浆的D0E（OP）D1漂白

D_0E_ ( OP ) D_1 Bleaching of High Kappa Number Bamboo Kraft Pulps

CMC辅助打浆对竹浆纤维特性及成纸性能的影响

Effects of CMC Addition during Beating Pulp of Bamboo on its Fiber and Paper Properties

对硫酸盐法竹浆次氯酸盐-二氧化氯（HD）漂白工艺进行了研究。

In this paper , bleaching of kraft bamboo pulp with HD short sequence was studied .

竹浆GIF仿酶漂白（Ⅱ）-仿酶预处理全无氯漂白

Bamboo Pulp GIF Biomimetic Bleaching (ⅱ) Totally Chlorine Free Bleaching with Biomimetic Pretreatment

漆酶用于硫酸盐竹浆TCF漂白的研究

Utilization of Laccase in TCF Bleaching of Kraft Bamboo Pulp

竹浆木聚糖酶预处理对常规CEH三段漂的影响

The effect of xylanase pretreatment on conventional CEH bleaching of bamboo pulp

硫酸盐法竹浆D0（EOP）D1漂白条件的优化

The optimization of kraft bamboo pulp D_0 ( EOP ) D_1 bleaching

硫酸盐竹浆高温高压过氧化氢漂白工艺的研究甜竹硫酸盐浆不同ECF流程漂白试验

Study on High Temperature & High Pressure Hydrogen Peroxide Bleaching Technology for Bamboo Kraft Pulp

结果表明，CMC可以提高纤维之间的润滑性，减少打浆过程中纤维的过多切断，促进竹浆纤维在打浆过程中的分丝帚化。

The results indicated that CMC acts like lubricant , and can promote fibrillation , protect the bamboo fiber from over cutting during beating process .

改性织物的UPF值从8.16提高到18.18，在一定程度上提高了竹浆织物的紫外线防护功能。

The UPF values were increased from 8.16 to 18.18 which improved the bamboo fabric anti-UV protection .

对KP竹浆进行了单段氧脱木素、酸处理、螯合预处理及H2O2补充漂白研究。

In this paper , the single stage oxygen delignification , acid pretreatment , chelating pretreatment and H_2O_2 bleaching of kraft bamboo pulp were studied .

研究了AKD在竹浆中的施胶特牲。

The sizing performance of alkyl ketene dimmer ( AKD ) in bamboo pulp was studied in this paper .

硫酸盐竹浆强化碱抽提浆料的性能变化为Kappa值下降率66.0%，白度升高率25.4%，粘度下降率9.3%。

Properties of bleached pulp showed on declining rates of 66.0 % in Kappa and 9.3 % in viscosity , increasing rate of 25.4 % in brightness .

与空白试样相比，CMC辅助打浆能提高竹浆的打浆度、保水值、纤维间的结合力及成纸强度。

Comparing with the control experiments , the CMC addition can increase the beating degree , WRV , and the bonding between the fibers as well as the paper strength .

竹浆残余木素在Co-salen仿酶系统催化氧化中的结构变化

Structural changes of bamboo pulp residual lignin caused by Co-salen biomimetic catalytic oxidation

应用气相色谱-质谱分析竹浆Co-salen仿酶漂白机理

Mechanism Analysis For Co-salen Biomimetic Bleaching of Bamboo Pulp by Gas Chromatography-Mass Spectrometry

大豆11S球蛋白酶解产物及对肌原纤维混合蛋白特性的影响竹浆纤维/精梳棉/大豆蛋白纤维赛络纱的生产

Properties and Effects of 11S Globulin Hydrolysates on Myofibrillar Protein Production of bamboo fiber / combed cotton / soybean protein fiber blended Siro yarn

结果表明，竹浆HD短序漂白工艺优于传统的CEH漂白工艺。

Results indicated the HD bleaching was superior to the conventional CEH bleaching for kraft bamboo pulp , the HD bleaching wholly substituted for the conventional CEH bleaching .

研究了硫酸盐竹浆氧脱木素的影响因素以及氧脱木素对ECF漂白流程的影响。

The paper investigates the factors of the oxygen delignification of sulfate bamboo pulp and the effect of the oxygen delignification on the ECF technological process .

对卡伯值为11.4的深度脱木素硫酸盐竹浆分别进行了DQP、D0（EOP）D1和CEH3种不同漂序的漂白。

In this study , the DQP , D0 ( EOP ) D1 and CEH bleaching of kraft bamboo pulp with a kappa number of 11.4 were carried out .

通过在APMP竹浆中浆内施胶和表面喷淋实验，比较了产物、原料TAD及外购的紫外线吸收剂UVA的抑制返黄效果，并分析了产物应用的工艺条件。

By sizing and surface spraying experiment in APMP bamboo pulps , the yellowing inhibition effect of final product , TAD and purchased UV-absorber was compared , and the application condition of final product was studied .

结果表明，在适宜的漂白剂用量下3种漂白竹浆的白度均达到80%，以DQP和D0（EOP）D1为代表的ECF漂白具有很好的白度稳定性。

The bleaching results showed that 80 % brightness are obtained by using the three different bleaching sequences . Both DQP and D0 ( EOP ) D1 bleaching present better brightness stability and delignification selectivity .

对于硫酸盐竹浆，TAED加入到H2O2的漂白中能有效的提高漂白效果，纸浆的白度从32.6%ISO提高到53.4%ISO，比单独使用H2O2时的白度40.2%ISO高了13.2%ISO。

The main conclusion are as the follows . The additive of TAED to the H2O2 bleaching can upgrade the brightness of the kraft bamboo pulp , from 32.6 % ISO to 53.4 % ISO , 13.2 % ISO higher than using H2O2 alone which can reach 40.2 % ISO .

打浆后发现，这3种漂白竹浆的强度性能都较好，其中D0（EOP）D1漂白竹浆的各项强度性能最佳。

The property testing of the sheets made of the bleached bamboo pulps indicated that all bleached pulps have very good strength properties , and the strength properties of the D0 ( EOP ) D1 bleached pulp are better than the others .

为了提高竹浆性能和减少环境污染，对福建丛生小径竹进行了实验室模拟延伸改良连续蒸煮（EMCC）和常规硫酸盐法蒸煮（CKC）的研究。

In an attempt to improve bamboo-pulp properties and reduce environmental impact , laboratory simulated extended modified continuous cooking ( EMCC ) and conventional kraft cooking ( CKC ) of bamboo of minor diameters growing in Fujian were carried out in this study .

在此条件下，漂后竹浆白度达到91.26%ISO，聚合度1207，动力粘度15.04mPa·s，α-纤维素含量94.17%，木质素含量0.75%。

The pulp brightness after bleaching can reach 91.26 % ISO with the degree of polymerization of 1207 , the viscosity of 15.04mPa · s and the α - cellulose content of 94.17 % .